1. One of the methods of producing titanium clad steel plates is hot rolling, which involves the formation of an iron-based material and a titanium cladding material, the coating has at least one cladding surface for the assembly of the edge plate, and the cladding material and cladding material for the base material is required. 20 to 30 g/m2 of Mo or V. It is heated at the melting point, oxidized between 50 degrees Celsius and 1050 degrees Celsius to reduce titanium oxides, and then hot rolled.
2. The oxide that needs to be added is MoO3.
3. The heating temperature is between 845 degrees Celsius and 1050 degrees Celsius.
4. The oxide V2O5 needs to be added.
5. The heating temperature is between 740 degrees Celsius and 1050 degrees Celsius.
This technology is actually a process of producing titanium-steel clad plates from titanium by hot rolling method, which has good cladding characteristics and economical production cost. In the production process of stainless steel clad plates, hot rolling is more popular and suitable for mass production. However, this is not suitable for the production of titanium-steel composite plates. This is because titanium is easy to react to, and at high temperatures, it may chemically react with air or other metals, so the characteristics of titanium require cladding during hot rolling. Good encapsulation is difficult to achieve. Therefore, in the production of titanium-steel clad sheets by hot rolling, other materials need to be added between the titanium and the base material to prevent the formation of compounds at the boundaries of titanium and iron. These metals are precious, so titanium-clad steel is also expensive.
Baoji Taicheng Clad Metal Materials Co., Ltd is a metal composite plate manufacturer. At present, the most widely used production method is the explosive compound method. The company has 2 explosion sites with an annual output of more than 20,000 tons. Products are exported to many overseas countries, you are welcome to consult and cooperate!